1)

1,2 tấn = 1200(kg)

5 tạ = 500(kg)

\(m_{CaCO_3} = 1200.80\% = 960(kg)\)

\(CaCO_3 \xrightarrow{t^o} CaO + CO_2\\ n_{CaCO_3\ pư} = n_{CaO} = \dfrac{500}{56}(mol)\\ \Rightarrow H = \dfrac{\dfrac{500}{56}.100}{960}.100\% = 93\%\)

1 (H)= 93,11%

2 (H)=88.08%

m cao=1.064(tấn)

==> m cr = 1.065(tấn)

%m cao = 56%

Ta có: m_CaCO3 = 500.80% = 400 (g)

m _{chất rắn} = 400.78% = 312 (g)

Theo ĐLBT KL, có: m_CO2 = 400 - 312 = 88 (g)

\(\Rightarrow n_{CO_2}=\dfrac{88}{44}=2\left(mol\right)\)

PT: \(CaCO_3\underrightarrow{t^o}CaO+CO_2\)

_____2_____________2 (mol)

\(\Rightarrow m_{CaCO_3\left(pư\right)}=2.100=200\left(g\right)\)

Bạn tham khảo nhé!

Giả sử loại đá vôi ban đầu nặng 100g
=>  m_CaCO3 = 95g ;  m_MgCO3 =1,28 g ; m _{tạp chất trơ} = 3,72 gam
=> n_CaCO3 = \(\dfrac{95}{100}\)=0,95 mol; n_MgCO3 = \(\dfrac{1,28}{24}=0,015\left(mol\right)\)mol
Khi nung thì xảy ra phản ứng:
CaCO3 ––(t°)––> CaO + CO2 ↑

MgCO3 ––(t°)––> MgO + CO2 ↑

Ta có: n_CO2 = 0,95+0,015=0,965cmol
Nếu đá vôi bị phân hủy hoàn toàn thì khối lượng giảm:

0,965.44=42,46g
Vì khối lượng chất rắn thu được giảm 40,22%

=> m _giảm =100.44,22%= 40,22g
Vậy tỉ lệ đá vôi bị phân hủy là \(\dfrac{40,22}{42,46}.100=94,72\%\)

Chọn đáp án C 

m C a C O 3 = 0 , 8 m

C a C O 3 ® CaO + C O 2

    a             a         a   (mol) 

44a = m – 0,78m Þ a = 0,005m

H % = 100 . 0 , 005 m . 100 % 0 , 8 m = 62 , 5 %

Giả sử có 100g đá

=> \(m_{CaCO_3}=\dfrac{100.80}{100}=80\left(g\right)\)

\(n_{CaCO_3}=\dfrac{80}{100}=0,8\left(mol\right)\)

Gọi số mol CaCO₃ phân hủy

PTHH: CaCO₃ --t^o--> CaO + CO₂

             a-------------->a--->a

=> m_Y = 100 - 44a (g)

=> m_CaO = 56a (g)

=> \(\dfrac{56a}{100-44a}.100\%=45,65\%\)

=> a = 0,6 (mol)

=> \(H=\dfrac{0,6}{0,8}.100\%=75\%\)

C

Ta có: \(m_{CaCO_3}=400.\dfrac{80\%}{100\%}=320\left(g\right)\)

Mà hiệu suất bằng 80%, suy ra:

\(m_{CaCO_{3_{PỨ}}}=320.\dfrac{80\%}{100\%}=256\left(g\right)\)

Ta có: \(n_{CaCO_3}=\dfrac{256}{100}=2,56\left(mol\right)\)

PTHH: \(CaCO_3\overset{t^o}{--->}CaO+CO_2\)

Theo PT: \(n_{CaO}=n_{CaCO_3}=2,56\left(mol\right)\)

=> \(m_{CaO}=2,56.56=143,36\left(g\right)\)

Ta có: \(m_{Ca_{\left(CaO\right)}}=2,56.40=102,4\left(g\right)\)

=> \(\%_{m_{Ca_{\left(CaO\right)}}}=\dfrac{102,4}{143,36}.100\%\approx73,7\%\)

Chọn A

lấy m=100g 
=> mCaCO3=80 => n=0.8 
n pứ=x => mCaO=56x 
56x/(56x+(0.8-x)*100+20)=0.4565 
=> x=0.6 =|> H=0.6/0.8=0.75=75%

\(1)PTHH:CaCO_3\xrightarrow{t^o}CaO+CO_2\uparrow\\ n_{CaCO_3}=\dfrac{500.95\%}{100}=4,75(mol)\\ \Rightarrow n_{CaO}=4,75(mol)\\ \Rightarrow m_{CaO}=4,75.56=266(g)\\ \Rightarrow m_{CaO(tt)}=266.80\%=212,8(g)\\ m_{CaCO_3(k p/ứ)}=500.95\%.20\%=95(g)\\ \Rightarrow m_A=95+212,8=307,8(g)\\ 2)\%m_{CaO}=\dfrac{212,8}{307,8}.100\%=69,136\%\\ n_{CO_2}=n_{CaO}=4,75(mol)\\ \Rightarrow V_{CO_2}=4,75.22,4=106,4(l)\)

mCaCO3= 80%. m(đá vôi)= 80%. 500=400(g)

-> nCaCO3= mCaCO3/M(CaCO3)=400/100=4(mol)

PTHH: CaCO3 -to-> CaO + CO2

Ta có: nCaO(LT)= nCaCO3= 4(mol)

=> mCaO(LT)=56.4=224(g)

Đặt x là số mol CaCO3 (p.ứ) -> Số mol CaO tạo thành là x (mol) (x>0)

=> Khối lượng rắn tạo thành là: 

(400 - 100x) + 56x + 100= 78%. 500

<=>x=2,5(mol) 

Vì KL tỉ lệ thuận số mol:

=> H(p.ứ)= (2,5/4).100= 62,5%