mCuO = 8 (g), mFe3O4 = 23,2
=> nCuO = 0,1 (mol), nFe3O4 = 0,1 (mol)
Bảo toàn Cu => nCu = nCuO = 0,1(mol) => mCu = 6,4(g)
Bảo toàn Fe => nFe = 3nFe3O4 = 0,3 (mol)=> mFe=16,8 (g)
Gọi nCO = x(mol) => nCO2.= x (mol)
Theo đlbtkl: mCO2 - mCO = moxit - mkloai = 31,2-6,4-16,8=8
=> 44x - 28y= 8 => x = 0,5 (mol)
=> VCO = VCO2 = 11,2(l)
a)
Gọi $m_{Fe_3O_4} = \dfrac{31,2 + 15,2}{2} = 23,2(gam)$
$\Rightarrow n_{Fe_3O_4} = 0,1(mol)$
$m_{CuO} = \dfrac{31,2 - 15,2}{2} = 8(gam)$
$\Rightarrow n_{CuO} = 0,1(mol)$
$Fe_3O_4 + 4CO \xrightarrow{t^o} 3Fe + 4CO_2$
$CuO + CO \xrightarrow{t^o} Cu + CO_2$
Theo PTHH :
$n_{Fe} = 3n_{Fe_3O_4} = 0,3(mol) \Rightarrow m_{Fe} =0,3.56 = 16,8(gam)$
$n_{Cu} = n_{CuO} = 0,1(mol) \Rightarrow m_{Cu} = 0,1.64 = 6,4(gam)$
b)
$n_{CO\ pư} = n_{CO_2} = 4n_{Fe_3O_4} + n_{CuO} =0,5(mol)$
$V_{CO\ pư} = V_{CO_2} = 0,5.22,4 = 11,2(lít)$
mCuO = 8 (g), mFe3O4 = 23,2
=> nCuO = 0,1 (mol), nFe3O4 = 0,1 (mol)
Bảo toàn Cu => nCu = nCuO = 0,1(mol) => mCu = 6,4(g)
Bảo toàn Fe => nFe = 3nFe3O4 = 0,3 (mol)=> mFe=16,8 (g)
Gọi nCO = x(mol) => nCO2.= x (mol)
Theo đlbtkl: mCO2 - mCO = moxit - mkloai = 31,2-6,4-16,8=8
=> 44x - 28y= 8 => x = 0,5 (mol)
=> VCO = VCO2 = 11,2(l)